Fire Clay And High Alumina Bricks

PRODUCT

Al2O3

 %

(Min.)

Fe2O3

  %

(Max.)

B.D.

Gm/cc

(Min.)

  A.P.

   %

(Max.)

C.C.S.

Kg/cm2

  (Min.)

RUL

Ta oC

  (Min.)

PCE

 SK

(oC)

PLC

%

(Max)

 

APPLICATION

 

SKG - 30

 

SKG - 40 

 

SKG 45 B

 

SKG  - 50 B

 

SKG 60 B

 

SKG 70 B

 

SKG 72 B

 

SKG - 77 10

 

SKG - 80 B

 

SKG - 90 B

 

SKG - 42 D

 

     SKG  - 45 D

 

         SKG-SILLIMANITE

 

  30

 

  40

 

  45

 

  50

 

  60

 

  70

 

  72

 

  77

 

  80

 

  90

 

  42

 

  45

 

 

  56

 

  2.50

 

  2.50

 

  2.50

 

  2.50

 

  3.00

 

  3.00

 

  2.50

 

  1.10

 

  3.50

 

  3.50

 

  1.80

 

  1.50

 

 

  1.50

 

 

  2.00

 

  2.10

 

  2.20

 

  2.30

 

  2.50

 

  2.60

 

  2.70

 

  2.75

 

  2.80

 

  2.85

 

  2.25

 

  2.25

 

 

  2.40

 

  25

 

  23

 

  22

 

  22

 

  23

 

  23

 

  22

 

  19

 

  23

 

  23

 

  16

 

  16

 

 

  21

 

 

   250

 

   300

 

   300

 

   350

 

   350

 

  400

 

  400

 

  700

 

  400

 

  400

 

  500

 

  500

 

 

  400

  

 

 

 1350

 

 1400

 

 1450

 

 1430

 

 1430

 

 1470

 

 1540

 

 1650

 

 1500

 

 1500

 

 1480

 

 1520

 

 

 1500

 

  30

 

  34

 

  34

 

  35

 

  36

 

  36

 

  36

 

  --

 

  36

 

  36

 

  34

 

  34

 

 

  36

 

+ 0.5 at 1450 o C /2hrs.

 

+ 0.5 at 1450 o C /2hrs.

 

+ 1.0 at 1450 o C /2hrs.

 

+ 1.0 at 1450 o C /2hrs.

 

+ 1.0 at 1600 o C /2hrs.

 

+ 3.0 at 1600 o C /2hrs.

 

+ 2.5 at 1600 o C /2hrs.

 

+ 1.40 at 1600 o C /2hrs.

 

+ 1.5 at 1600 o C /2hrs.

 

+ 1.5 at 1600 o C /2hrs.

 

+ 0.5 at 1450 o C /2hrs.

 

+ 0.5 at 1450 o C /2hrs.

 

 

+ 1.0 at 1450 o C /2hrs.

 

 

GENERAL PURPOSE FIRE CLAY BRICK

 

 

 

FOR CEMENT PLANT & GENERAL APPLICATION

 

 

CEMENT PLANT ROTARY KILN & OTHER

APPLICATION

FOR BURNING ZONE OF CEMENT ROTARY

KILN & STEEL LADLE

SAME AS  ABOVE  BUT WITH BETTER PERFORMANCE

FOR PRE-BURNING & BURNING ZONE

 

FOR CEMENT & STEEL INDUSTRY

 

FOR STEEL & OTHER INDUSTRY

 

FOR STEEL, CEMENT & OTHER INDUSTRY

 

BLAST FURNACE.& ALUMINIUM INDUSTRY

 

 

GLASS TANK FURNACE & OTHER APPLICATION

 

 * ALL THE ABOVE DATA PERTAINS TO STANDARD PRESSABLE SHAPES SUBJECT TO REASONABLE VARIATIONS.

 * SIZE TOLERANCE + 1.5% OR 2.0 mm WHICHEVER IS GREATER.

 * BRICKS WITH PROPERTIES OF HIGHER VALUES AVAILABLE WHERE APPLICATIONS REQUIRE THE SAME.