Fire Clay And High Alumina Bricks
PRODUCT
|
Al2O3 % (Min.) |
Fe2O3 % (Max.) |
B.D. Gm/cc (Min.) |
A.P. % (Max.) |
C.C.S. Kg/cm2 (Min.) |
RUL Ta oC (Min.) |
PCE SK ( o C) |
PLC % (Max) |
APPLICATION
|
SKG SILLIMANITE -60D
SKG – 62 D
SKG–MULLITE
SKG – 85 D
SKG – 88 D
SKG – 95 D
SKG – 99 D
|
60
62
72
85
88
95
99 |
1.80
1.50
0.80
1.50
1.70
0.50
0.20 |
2.30
2.45
2.55
2.80
3.00
3.10
3.10 |
20
16
18
19
18
16
16 |
600
700
600
700
800
800
800
|
1550
1600
1750
1600
1600
1680
1680 |
36
36
36
36
36
40
40 |
+ 0.2 at 1450 o C /2hrs.
+ 0.2 at 1450 o C /2hrs.
+ 0.5 at 1600 o C /2hrs.
+ 0.5 at 1600 o C /2hrs.
+ 0.3 at 1600 o C /2hrs.
+ 0.5 at 1500 o C /2hrs.
+ 0.2 at 1500 o C /2hrs.
|
BLAST FURNACE STOVE & OTHER APPLICATION
BLAST FURNACE BOTTOM LINING
BLAST FURNACE, STOVE CHECKER , GLASS TANK CHECKER SPONGE IRON PLANT
BOTTOM OF REHEATING FURNANCE
FOR VERY SPECIAL APPLICATION
FOR PETROCHEMICAL & FERTILIZER INDUSTRY |
* ALL THE ABOVE DATA PERTAINS TO STANDARD PRESSABLE SHAPES SUBJECT TO REASONABLE VARIATIONS.
* SIZE TOLERANCE + 1.5% OR 2.0 mm WHICHEVER IS GREATER.
* BRICKS WITH PROPERTIES OF HIGHER VALUES AVAILABLE WHERE APPLICATIONS REQUIRE THE SAME.