Magnesia Carbon Bricks
|
MgO % (INFM*/DBM Used) |
F C % (Min.) |
B.D. Gm/cc (Min.) |
A.P. % (Max.) |
C.C.S. kg/cm2 (Min.) |
A.P (%) (Max. coked at 1000 oC) |
MOR Kg/cm2 RT |
HMOR At 1400 oC/ ½ hrs. |
APPLICATION |
SKG-MAGCARB-9805 SKG-MAGCARB-9808 SKG-MAGCARB-9812 SKG-MAGCARB-9818
SKG-MAGCARB-9705 SKG-MAGCARB-9708 SKG-MAGCARB-9712 SKG-MAGCARB-9718
SKG-MAGCARB-9605 SKG-MAGCARB-9608 SKG-MAGCARB-9612 SKG-MAGCARB-9618
SKG-MAGCARB-9308 SKG-MAGCARB-9208 SKG-MAGCARB-9205 SKG-MAGCARB-9008
|
98* 98* 98* 98*
97* 97* 97* 97*
96* 96* 96* 96*
93 92 92 90 |
5 8 12 18
5 8 12 18
5 8 12 18
8 8 5 8 |
3.02 2.98 2.92 2.88
3.00 2.95 2.90 2.85
3.00 2.95 2.90 2.85
2.85 2.85 2.85 2.80 |
5 5 5 6
5 5 5.5 6
6 6 6.5 7
7 7 7 7.5 |
500 450 400 350
500 450 400 350
500 450 400 350
400 350 400 300 |
10 10 11 12
11 12 13 13
10 10 11 12
14 14 14 14 |
160 150 140 130
150 130 120 100
140 120 110 110
100 90 100 100 |
90-120 90-120 90-110 90-110
80-100 80-100 80-100 80-100
80-90 80-90 80-90 80-90
50-70 50-70 50-70 30-40 |
BOF Lining , steel Ladle, slag area and EAF . Hot Spot
|
BOF Lining , steel Ladle, slag area and EAF . Hot Spot
|
|||||||||
STEEL LADLE SLAG ZONE
|
|||||||||
STEEL LADLE METAL ZONE AND BOTTOM |
* ALL THE ABOVE DATA PERTAINS TO STANDARD
PRESSABLE SHAPES SUBJECT TO REASONABLE VARIATIONS.
* SIZE TOLERANCE +
1.5% OR 2.0 mm WHICHEVER IS GREATER.
* BRICKS WITH PROPERTIES OF HIGHER VALUES
AVAILABLE WHERE APPLICATIONS REQUIRE THE SAME.