Magnesite Chrome, Chrome Magnesite,
Chromite Bricks
PRODUCT
|
MgO % (Min.) |
Cr2O3 % (Min) |
SiO2. % (Max.) |
Fe2O3 % (Max.) |
A.P. % (Max.) |
C.C.S. Kg/cm2 (Min.) |
RUL Ta o C (Min.) |
PLC(%) At 1600 oC/ 2hrs. |
APPLICATION
|
MAGNESITE CHROME
SKG MCH
SKG - MCH (D)
SKG CEMAC
SKG CEMAC-BZ
CHROME MAGNESITE
SKG CHM
SKG CHM (S)
SKG CHM (D)
CHROMITE
SKG CHT
SKG CROME L-D
|
60
65
70
80
40
45
50
--
-- |
15
10
8
3 5
18
22
30
40
40 |
--
--
--
--
--
--
--
--
-- |
--
--
--
--
--
--
--
--
--
|
23
20
22
19
24
23
22
21
18 |
350
400
400
550
300
350
400
500
600 |
1560
1600
1600
1600
1550
1600
1650
1480
1400 |
0.5
0.5
0.5
0.5
0.5
0.5
0.5
0.5
0.2 |
FOR GENERAL APPLICATION
A.O.D./V.O.D./LRF
ALKALI RESITANT BRICK FOR CEMENT PAPER & CHEMICAL INDUSTRY CEMENT ROTARY KILN BURNING ZONE BRICK
FOR GENERAL APPLICATION
FOR HIGH TEMPERATURE APPLICATION SUCH AS EAF
FOR HIGHER TEMPERATURE APPLICATION SUCH AS EAF
ABRASION RESISTANT QUALITY BRICKS FOR HEARTH OF SOAKINGPIT AND REHEATING FURNANCE SAME AS ABOVE BUT DENSE QUALITY |
* ALL THE ABOVE DATA PERTAINS TO STANDARD PRESSABLE SHAPES SUBJECT TO REASONABLE VARIATIONS.
* SIZE TOLERANCE + 1.5% OR 2.0 mm WHICHEVER IS GREATER.
* BRICKS WITH PROPERTIES OF HIGHER VALUES AVAILABLE WHERE APPLICATIONS REQUIRE THE SAME.